24KU1043

利用課題名 / Title

Research on nano-silica modified epoxy resin properties and ageing resistance in hygrothermal conditions.

利用した実施機関 / Support Institute

九州大学 / Kyushu Univ.

機関外・機関内の利用 / External or Internal Use

内部利用（ARIM事業参画者以外）/Internal Use (by non ARIM members)

技術領域 / Technology Area

【横断技術領域 / Cross-Technology Area】（主 / Main）物質・材料合成プロセス/Molecule & Material Synthesis（副 / Sub）-

【重要技術領域 / Important Technology Area】（主 / Main）次世代ナノスケールマテリアル/Next-generation nanoscale materials（副 / Sub）マルチマテリアル化技術・次世代高分子マテリアル/Multi-material technologies / Next-generation high-molecular materials

キーワード / Keywords

コンポジット材料/ Composite material

利用者と利用形態 / User and Support Type

利用者名（課題申請者）/ User Name (Project Applicant)

CHEN Lirong

所属名 / Affiliation

九州大学大学院工学府土木工学専攻 　建設設計工学研究室

共同利用者氏名 / Names of Collaborators in Other Institutes Than Hub and Spoke Institutes

ARIM実施機関支援担当者 / Names of Collaborators in The Hub and Spoke Institutes

梶原隆司,深堀 明博

利用形態 / Support Type

（主 / Main）機器利用/Equipment Utilization（副 / Sub）,技術補助/Technical Assistance

利用した主な設備 / Equipment Used in This Project

KU-501：電子状態測定システム
KU-513：ゼータ電位・粒径・分子量測定装置群

報告書データ / Report

概要（目的・用途・実施内容）/ Abstract (Aim, Use Applications and Contents)

The purpose of this experiment is to compare the chemical bond between the neat and nano-silica modified epoxy resin.

実験 / Experimental

結果と考察 / Results and Discussion

The XPS spectra were examined to determine whether the incorporation of nano-silica affected the chemical structure of the epoxy resin. Results show the C1s core-level spectra of the neat epoxy resin and nano-silica modified epoxy resin. The XPS spectra of both specimens exhibited two fitted peaks at 284.8 eV and 286.4 eV, attributed to C–C/C–H and C–O bonds, respectively. In the epoxy resin sample modified with nano-silica, no significant peak was observed at 284.2 eV (C–Si bond). With the proportion of nano-silica growth, there is still no cpnpiscouos change in C1s core-level spectra of modified epoxy resin, we can draw a conclusion that nano-silica did not establish noticeable covalent bonding with the epoxy resin backbone.

図・表・数式 / Figures, Tables and Equations

その他・特記事項（参考文献・謝辞等） / Remarks(References and Acknowledgements)

成果発表・成果利用 / Publication and Patents

論文・プロシーディング（DOIのあるもの） / DOI (Publication and Proceedings)

口頭発表、ポスター発表および、その他の論文 / Oral Presentations etc.

特許 / Patents

特許出願件数 / Number of Patent Applications：0件
特許登録件数 / Number of Registered Patents：0件